Evolution of the structural and magnetic properties of sputtered Tb_xFe_73Ga_27-x (7 at.% ? x ? 11 at.%) thin films upon the increase of Tb content.
|
|
Autores:
|
Ranchal Sánchez, Rocío ;
Fin, S. ;
Bisero, D.
|
|
Tipo de documento:
|
texto impreso
|
|
Editorial:
|
Elsevier Science SA, 2016-05-15
|
|
Dimensiones:
|
application/pdf
|
|
Nota general:
|
info:eu-repo/semantics/openAccess
|
|
Idiomas:
|
|
|
Palabras clave:
|
Estado = Publicado
,
Materia = Ciencias: Física: Física de materiales
,
Tipo = Artículo
|
|
Resumen:
|
Tb_xFe_73Ga_27-x (7 at.% ? x ? 11 at.%) ternary alloys have been obtained by cosputtering from Tb_33Fe_67 and Fe_72Ga_28 targets. In contrast with other Tb-Fe-Ga compounds that consist of just one structural phase, the diffraction pattern of the Tb_7Fe_73Ga_20 shows the presence of two different phases related to binary Tb -Fe and Fe-Ga alloys. This microstructure evolves as the Tb content is increased, and for a Tb of 11 at.% X-ray diffractometry only evidences the presence of a phase close to the TbFe_2. Although none of the studied samples show perpendicular magnetic anisotropy, there is a significant component of the magnetization perpendicular to the sample plane. The increase of the Tb content on the compounds from 7 at.% to 11 at.% enhances this component most probably due to the shift of the microstructure towards one similar to the TbFe_2.
|
|