Defect and nanocrystal cathodoluminescence of synthetic opals infilled with Si and Pt
|
|
Autores:
|
Díaz-Guerra Viejo, Carlos ;
Kurdyukov, D.A. ;
Piqueras de Noriega, Javier ;
Sokolov, V. I. ;
Zamoryanskaya, M. V.
|
|
Tipo de documento:
|
texto impreso
|
|
Editorial:
|
American Institute of Physics, 2001-03-01
|
|
Dimensiones:
|
application/pdf
|
|
Nota general:
|
info:eu-repo/semantics/openAccess
|
|
Idiomas:
|
|
|
Palabras clave:
|
Estado = Publicado
,
Materia = Ciencias: Física: Física de materiales
,
Tipo = Artículo
|
|
Resumen:
|
Synthetic opals-composed of 250 nm amorphous silica spheres closed packed in a face centered cubic structure-have been infilled with silicon, platinum, and with Si and different Pt contents. The luminescent properties of these composites have been investigated by cathodoluminescence (CL) microscopy and spectroscopy. CL emission is influenced by the material used to infill the pores of the opal matrix. CL spectra of all the samples investigated show two well-known bands, associated with the defect structure of the silica spheres, centered at about 1.9 and 2.7 eV, respectively. Emission in the 2.15-2.45 eV range, particularly intense in opal-based composites with a high Pt content, is tentatively associated with SiO2 defects involving silicon clusters. A CL band peaked at about 3.4 eV as well as a band in the 1.50-1.75 eV range, whose peak position seems to be affected by the Pt content of the samples, are associated with the presence of Si nanocrystals. The behavior of these emissions suggests that both are related to defect states at the interface between Si nanocrystals and SiO2 forming the opal spheres.
|
|