Cathodoluminescence of defects in sintered tin oxide
|
|
Autores:
|
Maestre Varea, David ;
Cremades Rodríguez, Ana Isabel ;
Piqueras de Noriega, Javier
|
|
Tipo de documento:
|
texto impreso
|
|
Editorial:
|
American Institute of Physics, 2004-03
|
|
Dimensiones:
|
application/pdf
|
|
Nota general:
|
info:eu-repo/semantics/openAccess
|
|
Idiomas:
|
|
|
Palabras clave:
|
Estado = Publicado
,
Materia = Ciencias: Física: Física de materiales
,
Tipo = Artículo
|
|
Resumen:
|
Cathodoluminescence (CL) in the scanning electron microscope (SEM) has been used to investigate the luminescence mechanisms in tin oxide. Sintered material prepared from high purity powder has been found to show a strong dependence of the CL emission on the thermal treatments applied during sample preparation. SEM images show the presence of nano and microcrystalline grains. The correlation of the grain size and morphology with the optical emission is analyzed by CL microscopy and spectroscopy. The main emission bands appear centered at about 2.58, 2.25, and 1.94 eV depending on the sintering treatment. CL images reveal that the 2.25 and the 2.58 eV bands are associated at specific crystal faces. The evolution of the luminescence bands with mechanical milling shows a complex evolution of the 1.94 and 2.58 eV emissions which is explained by formation and recovery of defects during milling.
|
|
En línea:
|
https://eprints.ucm.es/id/eprint/23292/1/CremadesAna30libre.pdf
|